====== POE ====== A polyolefin is a type of polymer produced from a simple olefin (also called an alkene with the general formula CnH2n) as a monomer. For example, polyethylene is the polyolefin produced by polymerizing the olefin ethylene. Polypropylene is another common polyolefin which is made from the olefin propylene. ===== Industrial polyolefins ===== Most polyolefin produced in the industrial scale are made via polymerization through the use of catalysts. One example is the use of Ziegler-Natta catalyst for the polymerization of ethylene to polyethylene. * Thermoplastic polyolefins: polyethylene (PE), polypropylene (PP), polymethylpentene (PMP), polybutene-1 (PB-1); * Polyolefin elastomers (POE): polyisobutylene (PIB), ethylene propylene rubber (EPR), ethylene propylene diene monomer (M-class) rubber (EPDM rubber) ===== Properties ===== Polyolefin properties range from liquidlike to rigid solids, and are primarily determined by their molecular weight and degree of crystallinity. Polyolefin degrees of crystallinity range from 0% (liquidlike) to 60% or higher (rigid plastics). Crystallinity is primarily governed by the lengths of polymer's crystallizable sequences established during polymerization. Examples include adding a small percentage of comonomer like 1-hexene or 1-octene during the polymerization of ethylene, or occasional irregular insertions ("stereo" or "regio" defects) during the polymerization of isotactic propylene. The polymer's ability to crystallize to high degrees decreases with increasing content of defects. Low degrees of crystallinity (0-20%) are associated with liquidlike-to-elastomeric properties. Intermediate degrees of crystallinity (20-50%) are associated with ductile thermoplastics, and degrees of crystallity over 50% are associated with rigid and sometimes brittle plastics. Polyolefin surfaces are not effectively joined together by solvent welding because they have excellent chemical resistance and are unaffected by common solvents. They can be adhesively bonded after surface treatment (they inherently have very low surface energies and don't wet-out well (the process of being covered and filled with resin)), and by some superglues (cyanoacrylates) and reactive (meth)acrylate glues. They are extremely inert chemically but exhibit decreased strength at lower and higher temperatures. As a result of this, thermal welding is a common bonding technique. Practically all polyolefins that are of any practical or commercial importance are poly-alpha-olefin (or poly-α-olefin or polyalphaolefin, sometimes abbreviated as PAO), a polymer made by polymerizing an alpha-olefin. An alpha-olefin (or α-olefin) is an alkene where the carbon-carbon double bond starts at the α-carbon atom, i.e. the double bond is between the #1 and #2 carbons in the molecule. Alpha-olefins such as 1-hexene may be used as co-monomers to give a alkyl branched polymer (see chemical structure below), although 1-decene is most commonly used for lubricant base stocks. 1-hexene, an example of an alpha-olefin Many poly-alpha-olefins have flexible alkyl branching groups on every other carbon of their polymer backbone chain. These alkyl groups, which can shape themselves in numerous conformations, make it very difficult for the polymer molecules to align themselves up side-by-side in an orderly way. This results in lower contact surface area between the molecules and decreases the intermolecular interactions between molecules. Therefore, many poly-alpha-olefins do not crystallize or solidify easily and are able to remain oily, viscous liquids even at lower temperatures. Low molecular weight poly-alpha-olefins are useful as synthetic lubricants such as synthetic motor oils for vehicles and can be used over a wide temperature range. Even polyethylenes copolymerized with a small amount of alpha-olefins (such as 1-hexene, 1-octene, or longer) are more flexible than simple straight-chain high-density polyethylene, which has no branching. The methyl branch groups on a polypropylene polymer are not long enough to make typical commercial polypropylene more flexible than polyethylene. ===== Reference URL ===== * https://en.wikipedia.org/wiki/Polyolefin